Abstract
Ceramics with the sodium zirconium phosphate or NZP type structure have potential as nuclear waste form and inert matrix materials. For both applications the material will be subjected to self-radiation damage from α-decay of the incorporated actinides. In this study, ion-beam irradiation using Au- and He-ions has been used to simulate the consequences of α-decay and the effects of irradiation on the structural and macroscopic properties (density and hardness) have been investigated. Irradiation by Au-ions resulted in a significant volume contraction of ∼7%, a reduction in hardness of ∼30% and a loss in long-range order at fluences above 1014Au-ions/cm2. In contrast, little effect on the material properties was noted for samples irradiated with He-ions up to a fluence of 1017ions/cm2. Thermal annealing was investigated for the highest fluence Au-ion irradiated sample and significant decomposition was observed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.