Abstract

Advanced High Strength Steels (AHSS) are key materials in the conception of car body structures, permitting to reduce their weight while increasing their behavior in crash conditions. Nevertheless, the weldability of AHSS presents some particular aspects, in that complex failure types involving partial or full interfacial failure can be encountered more often than with conventional mild steels during destructive testing, despite high spot weld strength levels. This paper aims at characterizing the behavior of different AHSS spot welds under two quasi-static loading conditions, tensile shear and cross tension, often used in the automotive industry for the determination of their weldability. Interrupted cross tension and tensile shear tests were performed and spot welds failure was investigated with optical micrographs, SEM fractography and 3D-tomography in order to follow the three-dimensional crack paths due to the complex loading modes. A limited number of failure zones and damage mechanisms could be distinguished for all steel grades investigated. Moreover, numerical simulation of the tests was used to better understand the stress state in the weld and the influence of geometrical features such as weld size on the occurrence of the different failure types.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.