Abstract
Concrete structure beam exposed to marine atmosphere environment easily suffers from carbonization corrosion and their true characterization is significant for their durability designs. In this work, concrete structure beam was exposed naturally for 7-years in a marine atmosphere environment of My Island (Qingdao, China) and their carbonization degree was characterized using the phenolphthalein (pH-value) and hydrochloric acid (HCl) titrations respectively to obtain their carbonation depth (Xd) and frontier (Xf). The results showed that the OPC concrete beam is only carbonized in its surface layer with a 3 mm carbonization depth while 6 mm Xf, both of which are smaller than the Xd (9 mm) and Xf (16 mm) of the concrete mixed with 50% slag replacement. The recommended carbonation amplification coefficients (Xf/Xd) of the OPC/slag-cement concretes are 2.1 and 1.8, respectively. The increased carbonization of the load-bearing concrete beam in the tension zone is greater than the reduction carbonization in the compression zone.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.