Abstract
This paper presents the investigation work on different polymeric materials used as insulation materials of conductors in a multicore instrumentation cable. Among differently colored materials, only the white one presented cracks after a few years of use. Isothermal and non-isothermal DSC measurements were performed on initial (non-used) and aged (in service used or laboratory aged) materials as well as on raw materials in order to characterize their stability and the ageing state after storage, use in service or laboratory ageing. As shown by the oxidation induction time values, a pronounced antioxidant loss occurred for all materials during storage or service; plus a strong effect of the ambient light on stability was observed for the white insulation material. Around 3% of filler, consisting mainly of TiO 2 particles (as revealed by SEM-XRF elemental analysis), was found in the white material. The higher degradability of the white material can be related to both the photocatalytic effect of the TiO 2 particles and rapid loss of stabilizers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.