Abstract The precipitate formation and behavior in nitrogen-containing high-entropy alloy of equiatomic CoCrFeMnNi were characterized. The presence of 0.95 at.% nitrogen led to the formation of Cr2N precipitate in the as-recrystallized N-CoCrFeMnNi, in which annealing temperature affected the fraction and size of the formed Cr2N particles. It was observed that the Cr2N exhibited a Kikuchi crystal orientation relation (OR) with the face-centered cubic (FCC) matrix, and the OR was noticed to be in the plane of {1 1 1}γ//{0 0 0 1}Cr2N and direction of 1 1 0 γ / / 1 1 ¯ 0 0 Cr2N.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.