Abstract
In the present study, we investigate the fundamental properties of CeO2 by selecting La3+ (57), and Dy3+ (66) as dopants with optimized average atomic number of 61.5, which lies in between Pm3+ (62) and Sm3+ (62) in accordance with the criteria for optimum doping. A system of co-doped ceria ceramics Ce1–x–yLaxDyyO2-δ ((x, y) = (0.00, 0.00), (0.025, 0.025), (0.05, 0.05), (0.075, 0.075), (0.10, 0.10), (0.00, 0.20) and (0.20, 0.00)) as electrolytes for intermediate temperature solid oxide fuel cells were successfully prepared by a well-known sol-gel auto-combustion route. In order to obtain dense samples, the prepared pellets were sintered in air at 1300°C for 4h using conventional furnace and relative densities of all the samples were found to be higher than 95%. Single phase cubic structure, microstructural density and elemental composition analysis of all the samples were studied by powder X-ray diffraction, scanning electron microscope and energy dispersive spectroscopy techniques, respectively. Raman spectroscopy analysis confirmed the formation of concentrated O2-–vacancies in the co-doped ceria system. Impedance spectroscopy measurements revealed the high value of total ionic conductivity and low activation energy for the composition Ce0.85La0.075Dy0.075O2−δ i.e., 2.08 × 10–2 S cm–1 and 0.58eV, respectively. Linear thermal expansion analyses of all the samples revealed the matched thermal expansion coefficients. Finally, these results recommend that the Ce0.85La0.075Dy0.075O2−δ sample can be useful as a solid electrolyte in IT-SOFC applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have