Abstract
This study examines the electronic and luminescent properties of β-(AlxGa1−x)2O3 (0 ≤ x ≤ 0.42) thin films grown on (0001) sapphire using laser-MBE, with a focus on the evolution of defect energy levels and their impact on surface Fermi level pinning and luminescence. X-ray photoelectron spectroscopy (XPS) and cathodoluminescence (CL) have been employed to analyze surface band bending and defect evolution as a function of aluminum content. The results have revealed a pinned Fermi level at 3.6 eV above the valence band maximum despite the increase in the bandgap. The consequent upward band bending has been confirmed by a peak shift in the core level XPS. The defects that lead to the Fermi level pinning effect are attributed to E2*, which is related to a Ga vacancy or Ga vacancy-O vacancy complex. In addition, CL spectroscopy and depth-resolved CL have demonstrated consistent blue and ultraviolet emissions across the Al content range and a similar suppression of electron concentration on blue and ultraviolet emissions in β-(AlxGa1−x)2O3 and β-Ga2O3. Based on the observed evolution of defects with Al content, the blue band emission is attributed to electron transition in the donor–accepter pair.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call