Investigation of the piezoelectric and anti-reduction properties of (Ba, Ca) (Ti, Sn, Hf) textured ceramics prepared under low oxygen partial pressure conditions at low sintering temperatures

Abstract

Multilayer piezoelectric ceramics must be sintered in a reducing atmosphere, preventing oxidation of the inner base metal. Plate-like textured (Ba, Ca)(Ti, Sn, Hf)O3 ceramics with a <001> preferred orientation were successfully developed at a low oxygen partial pressure (PO2:10−8 atm) using a BaTiO3 (BT) template with sintering temperatures < 1300 °C, which is beneficial for multilayer applications using base metal co-firing with ceramics. When adding the 3 wt% BT template, the proposed samples had a Lottgering factor of 84 %, piezoelectric coefficients d33 = 324 pC/N, -d31 = 122 (pC/N), and Qm = 452, and the strain values increased from 0.07 % for the randomly oriented ceramics to 0.115 % at 20 kV/cm for the textured ceramics, confirming that the texturing behavior assisted the grain growth and improved both the soft and hard behaviors and insulation resistance of the proposed lead-free ceramics. These findings make a significant contribution to the production of high-power piezoelectric components.