Abstract
The results of studies of the diffusion interaction of titanium with aluminum at a temperature of 650 ° C are presented. The phase and chemical composition of the diffusion interaction zone and the nature of changes in its thickness from the exposure time are determined. It is shown that accelerated cooling of explosion-welded composites from the heat treatment temperature leads to spontaneous separation of the aluminum layer with the formation of a coating based on intermetallic TiAl on the titanium surface.