Abstract
The studies results of the titanium with aluminum diffusion interaction at a temperature of 650 oC are presented. The phase and chemical composition of the diffusion interaction zone, the nature of the change in its thickness from the exposure time are determined. It is shown that accelerated cooling of explosion-welded composites from the heat treatment temperature leads to spontaneous separation of the aluminum layer with the formation of a coating based on the TiAl3 intermetallic compound on the titanium surface.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.