Abstract
In this work, a SiGeSn/GeSn/SiGeSn single quantum well was grown and characterized. The sample has a thicker GeSn well of 22nm compared to a previously reported 9nm well configuration. The thicker well leads to: (i) lowered ground energy level in Γ valley offering more bandgap directness; (ii) increased carrier density in the well; and (iii) improved carrier collection due to increased barrier height. As a result, significantly enhanced emission from the quantum well was observed. The strong photoluminescence (PL) signal allows for the estimation of quantum efficiency (QE), which was unattainable in previous studies. Using pumping-power-dependent PL spectra at 20K, the peak spontaneous QE and external QE were measured as 37.9% and 1.45%, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.