Abstract
Mechanical alloying (MA) of elemental Al and Cr powders of nominal composition Al86Cr14 has been performed by using a conventional ball – mill. The MA process produced a supersaturation of Cr in Al. Isothermal annealing at 590 °C represented in the formation of quasicrystalline phase, in addition of two intermetallic phases Al13C2 and Al14.Cr. A supersaturation solid solution of a α- Fe (AI) and a metastable Al6 Fe phase were formed by MA of a mixture of Al and Fe elements containing of nominal composition Al84 Fe16. However, thermal treatment fail to produce the quasi-phase, various intermetallic phase are obtained. For both alloy systems, milling structure have a nano size of ≈25 nm for Al86Cr14 and ≈37 nm for Al84Fe16, the thermal stability of the produced phases was also examined.
Highlights
Summary
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.