Abstract
Positron lifetime, annihilation line shape, and electron microscopic measurements have been carried out on neutron irradiated pressure vessel steel (HSST Plate 03) meeting ASTM A533-B (Unified Numbering System [UNS] K12539). The positron annihilation parameters for specimens irradiated at 423 K to a dose of 1.5 × 1018 n/cm2 are found to decrease sharply during the post-irradiation annealing interval, 473 to 623 K. This correlates well with the stage seen in the recovery of Vickers hardness. On the basis of known evidence for carbon migration in α-iron and the interpretation of present results, enhancement and recovery of radiation hardening have been qualitatively understood in terms of formation and dissolution of carbon decorated vacancy complexes.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.