Investigation of mechanical properties of masterbatches and composites with small additions of CNTs

Abstract

The present paper investigated physical and mechanical properties of the nanotube masterbatches and the polymer composites with low contents of carbon nanotubes (CNTs), which were obtained by diluting masterbatches. Ethylene-octene copolymer was used as the binder for the masterbatches, which provides the elasticity of the material at a content 20 wt% of CNT. Masterbatches were obtained with a 2-roller mixer, and their additive to polypropylene was carried out on a single screw injection molding machine. Strength properties of ethylene-octene copolymer increased when additing CNTs in an amount of 5-20 wt%. When the concentration of CNT in masterbatches is reduced to 0.01-0.1 wt% its strength characteristics increased up to 4-18%. The most effective strengthening of polypropylene was observed with the content of CNTs 0.1 wt%.