Abstract
Friction stir welding (FSW) of 6-mm-thick plates of AA6061-T651 was carried out using a simple cylindrical pin tool. The impact of welding factors (rotational speed, welding speed) on tensile properties, microhardness, and surface roughness of FSW joints was investigated. Ultimate tensile strength (UTS), yield strength, and % elongation of AA6061-T651 base plate as well as FSW joints were found out using a universal testing machine (UTM). Maximum value of UTS and yield strength were achieved at rotational speed of 1400 rpm and welding speed of 20 mm/min. Minimum surface roughness was reached at rotational speeds of 1400 rpm and welding speed of 20 mm/min. Microstructural evolutions in the friction stir welded (FSWed) joint and microhardness profile were also determined. Maximum hardness of HV 120 was acquired for the stir zone (SZ). Hence, attainment of the maximum tensile strength, microhardness, and minimum surface roughness during FSW is a desired method to improve the service life and suitability of AA6061-T651.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Mechanical and Materials Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.