Abstract

The mechanical properties, glass-forming ability, supercooled liquid region and devitrification behaviour of the Cu–Zr–Ti–(Pd, Ag, Pt and Au) bulk glass formers were studied by using a mechanical testing machine, X-ray diffraction, transmission electron microscopy, differential scanning calorimetry and isothermal calorimetry. The bulk glassy alloys of diameter 2 mm were formed in the Cu55Zr30Ti10Pd5 and Cu55Zr30Ti10Ag5 alloys while Cu55Zr30Ti10Au5 bulk alloy showed mixed glassy and crystalline structure. No glassy phase was formed in the Cu55Zr30Ti10Pt5 bulk alloy whereas the glassy phase was formed in all of the ribbon samples prepared by rapid solidification. The studied alloys except for the Pt-bearing one have slightly increased compressive fracture or yield strength values compared to ternary Cu60Zr30Ti10 glassy alloy. At the same time Pd and Au addition significantly expand the supercooled liquid region of Cu–Zr–Ti glassy alloy and increase Young’s modulus. A nanoicosahedral phase is primarily formed in the Cu55Zr30Ti10(Pd,Au)5 glassy alloys in the initial stage of the devitrification process by nucleation and three-dimensional diffusion-controlled growth. Nearly the same quasilattice constant obtained in the Cu55Zr30Ti10(Pd,Au)5 alloys illustrates the same type of the icosahedral phase in these alloys. However, no icosahedral phase was found in the Cu55Zr30Ti10(Ag,Pt)5 alloys.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.