Abstract
Multilayer graphene (MLG) shows an attractive prospect for the demanding engineering applications. This paper reports the mechanical and tribological properties of MLG reinforced Ni3Al matrix composites (NMCs) under dry sliding at varying sliding speed. The hardness and elastic modulus of the NMCs are significantly influenced with MLG content. It is found that the hardness and elastic modulus of the NMCs are found to be increased by increasing MLG content up to 1.0wt.%, while decreased when MLG content is above 1.0wt.%. Tribological experiments suggest that MLG can dramatically improve the wear resistance and decrease the friction coefficient of the NMCs. Such marked improvement of wear resistance is attributed to the reinforcing mechanisms of MLG, such as crack deflection and pull-out, and reduction of friction coefficient is related to the formation of a tribofilm on the sliding contact surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.