Abstract
Arc brazing is an alternative joining technology well-suited for processing thermally sensitive materials and to produce mixed material connections. Due to the technological similarities of gas metal arc brazing to gas metal arc welding, it can be assumed that the process-related hydrogen input is of similar magnitude for both joining technologies. Since diffusible hydrogen is known to cause embrittlement in metallic materials, it is necessary to know the amount of diffusible hydrogen introduced by different manufacturing processes. Regarding the qualification of welding procedures, hydrogen ingress is an important factor to evaluate the risk of hydrogen-assisted cold cracking, especially when processing high-strength steels. For arc brazing, there is a lack of knowledge about the process-related hydrogen input. Hence, to study the influence of different brazing filler materials and varying levels of heat input on the diffusible hydrogen concentration in arc braze metal, a methodology to determine hydrogen content in arc weld metal in accordance with international standard ISO 3690 based on carrier gas hot extraction was applied to arc brazed specimens. Very low diffusible hydrogen concentrations of about HD = 0.1 to 0.3 mL/100 g were found for GMAB without significant influence of arc energy or filler metal used.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.