Abstract
Deep cryogenic heat treatment is a supplementary process, which is performed in tool steels after quench and before temper regularly. In this study, the effect of the electric current flow through the deep cryogenically treated samples was investigated via the X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscope (EDX), hardness test, and pin-on-disk wear testing machine. Results showed that the deep cryogenic heat treatment improves the carbide percentage, distribution, hardness and wear resistance of the 1.2080 tool steel, as compared with those of the conventionally treated. Further improvement in the wear resistance and hardness were also observed due to the formation of some newly formed nano-sized carbides in the structure. It was also observed that the electric current flow leads to a decrease in this improvement due to its effect on the as-quench vacancies, which were ignored as powerful places for carbide nucleation during the deep cryogenic heat treatment. It was also shown that the predominant wear mechanism is a combination of adhesive and tribo-chemical wear.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.