Abstract
The bistability characteristics of GaN/AlN resonant tunneling diodes (RTDs) grown on a sapphire substrate by metalorganic vapor phase epitaxy (MOVPE) were investigated to better understand their physical origin and explore their use in nonvolatile memories. The bistability current–voltage (I–V) characteristics of GaN/AlN RTDs, which were due to intersubband transitions and electron accumulation in the quantum well, were clearly observed over a wide temperature range between 50 and 300 K. However, the I–V characteristics sometimes degraded at temperatures above 250 K. Complex staircase structures were observed in the voltage region showing a negative differential resistance in the I–V curve, and the forward current increased or decreased rapidly as the forward-bias voltage increased. Repeated measurements of the I–V characteristics over the wide temperature range between 50 and 300 K revealed that the bistability characteristics of GaN/AlN RTDs degraded owing to the leakage of electrons accumulating in the quantum well through a deep level in the AlN barrier associated with crystal defects such as dislocations and impurities. Therefore, reduction in crystal defect and impurity densities in the AlN barrier, and a careful design that considers deep levels are important for realizing realize ultrafast nonvolatile memories based on the bistability characteristics of GaN/AlN RTDs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have