Investigating laser rapid manufacturing for Inconel-625 components

Abstract

This paper presents an investigation of laser rapid manufacturing (LRM) for Inconel-625 components. LRM is an upcoming rapid manufacturing technology, it is similar to laser cladding at process level with different end applications. In general, laser-cladding technique is used to deposit materials on the substrate either to improve the surface properties or to refurbish the worn out parts, while LRM is capable of near-net shaping the components by layer-by-layer deposition of the material directly from CAD model. In the present study, a high-power continuous wave (CW) CO 2 laser system, integrated with a co-axial powder-feeding system and a three-axis workstation were used. The effect of processing parameters during LRM of Inconel-625 was studied and the optimum set of parameters for the maximum deposition rate was established employing Orthogonal L9 array of Taguchi technique. Results indicated that the powder feed rate and the scan speed contributed about 56% and 26%, respectively to the deposition rate, while the influence of laser power was limited to 10% only. Fabricated components were subjected to non-destructive testing (like—ultrasonic testing, dye-penetrant testing), tensile testing, impact testing, metallographic examinations and micro-hardness measurement. The test results revealed defect-free material deposition with improved mechanical strength without sacrificing the ductility.