Abstract
Gallium arsenide (GaAs) implanted with silicon forming intersubband of SiGaAs is a promising material for making novel electronic and optoelectronic devices. This paper is focused on finding optimum fluence condition for formation of intersubband of SiGaAs in GaAs sample after implantation with 50[Formula: see text]keV silicon negative ions with fluences varying between [Formula: see text] and [Formula: see text] ions cm[Formula: see text]. The GaAs samples were investigated using X-ray photoelectron spectroscopy (XPS), UV-Vis.-NIR spectroscopy and X-ray diffraction (XRD) techniques. The X-ray photoelectron spectra for unimplanted sample showed peaks at binding energy of 18.74[Formula: see text]eV and 40.74[Formula: see text]eV indicating Ga3d and As3d core level, whereas the corresponding core level peaks for implanted sample were observed at binding energy of 19.25[Formula: see text]eV and 41.32[Formula: see text]eV. The shift in Ga3d and As3d core levels towards higher binding energy side in the implanted sample with respect to unimplanted sample were indicative of change in chemical state environment of Ga–As bond. The relative atomic percentage concentration of elemental composition measured using casa XPS software showed change in As/Ga ratio from 0.89 for unimplanted sample to 1.13 for sample implanted with the fluence of [Formula: see text] ion cm[Formula: see text]. The UV-Vis-NIR spectra showed absorption band between 1.365[Formula: see text]eV and 1.375[Formula: see text]eV due to the formation of intersubband of SiGaAs for fluences greater than [Formula: see text] ion cm[Formula: see text]. The GaAs crystallite size calculated using Brus formula was found to vary between 162[Formula: see text]nm and 540[Formula: see text]nm, respectively. The XRD spectra showed the presence of Bragg’s peak at 53.98∘ indicating (311) silicon reflection. The silicon crystallite size determined from full width at half maxima (FWHM) of (311) XRD peak was found to vary between 110[Formula: see text]nm and 161[Formula: see text]nm, respectively.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.