Abstract
The oxidation of single crystal gallium nitride in dry air has been investigated. X-ray photoelectron spectroscopy (XPS) revealed minimal oxide growth at 450 and 750 °C for up to 25 h. However, at 900 °C the growth of an oxide approximately 5000 Å thick was observed after 25 h. This oxide was determined to be the monoclinic β-Ga2O3 using glancing angle x-ray diffraction. XPS spectra of the Ga 3d and Ga 2p core levels indicated peak shifts of 1.2 and 1.3 eV, respectively, from Ga–O to Ga–N bonding. The Ga L3M45M45 core level binding energy was also investigated and β-Ga2O3 and GaN each presented a characteristic peak shape.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.