Abstract
The interfacial reactions in a Sn-20In-2.8Ag solder ball grid array (BGA) package with immersion Ag surface finish are investigated. After reflow, the Ag thin film dissolves quickly into the solder matrix, and scallop-shaped intermetallic layers, with compositions of (Cu0.98Ag0.02)6(In0.59Sn0.41)5, appear at the interfaces between Sn-20In-2.8Ag solder ball and Cu pad. No evident growth of the (Cu0.98Ag0.02)6(Sn0.59In0.41)5 intermetallic compounds was observed after prolonged aging at 100 °C. However, the growth accelerated at 150 °C, with more intermetallic scallops floating into the solder matrix. The intermetallic thickness versus the square root of reaction time (t 1/2) shows a linear relation, indicating that the growth of intermetallic compounds is diffusion-controlled. Ball shear tests show that the strength of Sn-20In-2.8Ag solder joints after reflow is 4.4 N, which increases to 5.18 N and 5.14 N after aging at 100 and 150 °C, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call