Abstract
AbstractIn this paper, short carbon fiber (SCF) interlaminar toughened carbon fiber reinforced epoxy resin (CF/EP) composite laminates were prepared. The effect of SCF content on the mode II interlaminar fracture toughness (GIIC) and flexural properties of CF/EP composites was investigated. It was shown that the addition of SCF between the plies had an effect on the GIIC of the composites. When the SCF content was 10 g/m2, the GIIC increased from 1506.62 J/m2 to 1995.6 J/m2, which improved by about 32.46%. When the content of SCF was 5 g/m2, the flexural strength and flexural modulus increased by 36.92% and 98.48%, respectively, showing the best performance. The toughening mechanism of SCF was observed by SEM images as SCF debonding and pulling out from the resin and SCF fracture. The present study was also compared with our previous study on short aramid fiber interlaminar toughened CF/EP composites, and the test data and SEM images of the two experiments were compared to analyze the effect of different short fibers on the interlaminar toughening effect, which provides some reference for the selection of interlaminar toughening materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.