Abstract
Microstructural studies on the interfacial boundaries of 1:1 and 1:2 ordered domains in (Ba 0.9 La 0.1 )(Mg 0.37 Nb 0.63 )O 3 were conducted using high-resolution transmission electron microscopy and X-ray diffractometry. Both 1:2 and 1:1 ordered domains coexisted in a fully ordered single grain. Each ordered domain occupied its own region, and the interfaces were atomically sharp and coherent. The wavelength of the superlattice modulation was ∼0.47 nm in the 1:1 ordered domain and ∼0.71 nm in the 1:2 ordered domain. The transition from the 1:2 ordered region to the 1:1 ordered region was clearly shown at the interface. These observations well support the structural models that have been previously presented.