Abstract
This study investigated the interfacial reactions between n-type Bi2(Te,Se)3 thermoelectric material, characterized by a highly-oriented (110) plane, and pure Sn and Sn-3.0Ag-0.5Cu (wt.%) solders, respectively. At 250 °C, the liquid-state Sn/Bi2(Te,Se)3 reactions resulted in the formation of both SnTe and BiTe phases, with Bi-rich particles dispersed within the SnTe phase. The growth of the SnTe phase exhibited diffusion-controlled parabolic behavior over time. In contrast, the growth rate was considerably slower compared to that observed with p-type (Bi,Sb)2Te3. Solid-state Sn/Bi2(Te,Se)3 reactions conducted between 160 °C and 200 °C exhibited similar interfacial microstructures. The SnTe phase remained the primary reaction product, embedded with tiny Bi-rich particles, revealing a diffusion-controlled growth. However, the BiTe layer had no significant growth. Further investigation into growth kinetics of intermetallic compounds and microstructural evolution was conducted to elucidate the reaction mechanism. The slower growth rates in Bi2(Te,Se)3, compared to the reactions with (Bi,Sb)2Te3, could be attributed to the strong suppression effect of Se on SnTe growth. Additionally, the interfacial reactions of Bi2(Te,Se)3 with Sn-3.0Ag-0.5Cu were also examined, showing similar growth behavior to those observed with Sn solder. Notably, compared with Ag, Cu tends to diffuse towards the interfacial reaction phases, resulting in a high Cu solubility within the SnTe phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.