Abstract
In this study, the effect of post-processing heat treatment on the interface morphology and kinetics of intermetallic phase growth in titanium/copper bimetallic sheets were analyzed using a scanning electron microscopy and mechanical testing. Ti/Cu composite was fabricated by explosive welding. Then, clads were subjected to the post-welded annealing at 973 K for times ranging between 15 min and 100h. In the as-bonded state, the interface shows a wavy character with a limited number of melted zones, which are mostly composed of phases that are not observed in the Ti-Cu equilibrium phase diagram. Short-term annealing is shown to transform non-equilibrium phases into equilibrium ones, such as TiCu4 and Ti3Cu4. For longer annealing times, the growth of four intermetallic sublayers (Ti2Cu, TiCu, Ti3Cu4, and TiCu4) distributed along the entire interface is detected. However, the growth kinetics of particular sublayers was different. Volume fraction estimation of intermetallic phases at annealing times under study revealed the largest thickness for TiCu and TiCu4 phases. The nano-hardness of intermetallic sublayers was found to drop with the Ti content.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.