Abstract
In this paper, rare earth Nd with various contents (0, 0.04 and 0.5 wt.%) was incorporated into Sn3.5Ag0.5Cu (SAC) solder. The influence of rare earth Nd on the interface reaction, microstructure development, mechanical behavior and wettability were investigated by scanning electron microscopy (SEM), joint strength measuring instrument, and wetting balance method. Adding a small amount of Nd can suppress the growth of interface IMC layer and subdivide the joint microstructure. The mechanical behavior and wettability were also improved efficiently. In the N2 atmosphere, the wettability of solder is better. In addition, the mechanical behavior of three kinds of solder joints decreases with increasing aging time, but the degree of decline of 0.04Nd solder joint is relatively slow.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.