We studied poly(lactic acid)’s strain-induced crystallization behavior during a tandem extrusion process using visualization techniques. Our visualization results showed that, despite its inherently slow crystallization kinetics in the quiescent condition, PLA crystallites were quickly formed inside the die at a temperature even above the melting temperature (Tm), as the melt temperature was decreased. Their rapid formation at a high temperature above the Tm peak, was due to the strain-induced crystallization. We also studied how the strain rate and the use of supercritical CO2 affected PLA crystallization. A significant increase in the PLA crystallization kinetics was caused by a sudden increase in the screw speeds of the extruders with a fixed barrel temperature. The crystallization enhancement, which was caused by the increased flow rate, became more pronounced at lower temperatures due to the higher degree of molecular orientation. Adding the CO2 shifted the crystallization temperature to a lower processing temperature due to its plasticization effect, but it accelerated the crystallization kinetics as well. We also observed a correlation between the content of the induced crystallites inside the extruder and the cellular structure of the extruded foams. This clearly explained the decrease in the optimal processing temperature for foaming with an increased CO2 content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.