Abstract

Wide bandgap semiconductors, particularly In2 O3 :Sn (ITO), are widely used as transparent conductive electrodes in optoelectronic devices. Nevertheless, due to the strohave beenng scattering probability of high-concentration oxygen vacancy (VO ) defects, the mobility of ITO is always lower than 40cm2 V-1 s-1 . Recently, hydrogen-doped In2 O3 (In2 O3 :H) films have been proven to have high mobility (>100cm2 V-1 s-1 ), but the origin of this high mobility is still unclear. Herein, a high-resolution electron microscope and theoretical calculations are employed to investigate the atomic-scale mechanisms behind the high carrier mobility in In2 O3 :H films. It is found that VO can cause strong lattice distortion and large carrier scattering probability, resulting in low carrier mobility. Furthermore, hydrogen doping can simultaneously reduce the concentration of VO , which accounts for high carrier mobility. The thermal stability and acid-base corrosion mechanism of the In2 O3 :H film are investigated and found that hydrogen overflows from the film at high temperatures (>250°C), while acidic or alkaline environments can cause damage to the In2 O3 grains themselves. Overall, this work provides insights into the essential reasons for high carrier mobility in In2 O3 :H and presents a new research approach to the doping and stability mechanisms of transparent conductive oxides.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.