Abstract
ABSTRACTThe initial stage of solid phase epitaxial (SPE) growth of GaAs films on the vicinal Si (001) substrate was investigated by high resolution transmission electron microscopy (H-RTEM). Cross-sectional [110] and [110] HRTEM images show that the SPE growth of crystalline GaAs islands from the amorphous phase proceeds via the formation of three-dimensional islands at the initial stage and islands' size and spacing are not critically dependent on the substrate tilt direction. The average vertical and lateral dimensions of islands were found to be 9 nm and 14 nm respectively, and the average island spacing was 10 nm. Moreover, many internal stacking faults (and/or microtwins) and a few dislocations have been already formed at this initial stage of growth. In addition, the critical thickness for misfit dislocation formation is found to depend upon the islands' lateral dimensions as well as the heights.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.