Abstract
Initial oxidation of HF-acid treated Si(1 0 0) surfaces with air exposure has been studied by using synchrotron radiation X-ray photoelectron spectroscopy. We demonstrate that the initial oxidation is explained not by a layer-by-layer process, but by a non-uniform mechanism. Just after dipping a Si substrate in HF-acid and spin-drying, the Si surface is immediately oxidized partly with a coverage of 0.2. It is considered that the non-uniform oxidation takes place at surface defects on H passivated Si surfaces. With increasing the air exposure up to 1 week, we have found that the non-oxidized part is oxidized uniformly at slower rates compared to the beginning. IR absorption spectroscopy with a multiple-internal-reflection geometry clearly indicates the backbond oxidation of surface Si takes place despite the H passivation produced by the HF-acid treatment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.