Abstract
In the present study, an evaluation method for the initial and progressive failure of composite laminates was proposed based on the Puck failure criterion and damage mechanics, respectively. In other words, the initial failure (crack initiation in the fiber and/or matrix) and progressive failure (crack growth in the fiber and/or matrix) were evaluated using the Puck failure criterion, and fiber- and matrix-dependent damage variables, respectively. In addition, the ABAQUS user-defined subroutine UMAT was developed based on coupling theories for the failure criterion and damage mechanics in order to efficiently analyze the progressive failure phenomenon in glass/carbon fiber-reinforced composite laminates. The developed subroutine was applied to the failure of industrial composite laminates, and the analysis results were compared to the experimental/numerical results previously reported in the literature. This comparative study confirmed that the simulation results were in good agreement with the reported composite failure results.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.