Abstract
Mass fraction of 1.5%, 3% of the nanomontmorillonite (MMT) were separately added in the phenol prepolymer, phenolic resin/ MMT was synthesized by in-situ method (it is called PF/M). The PF/M was carried out TG analysis using thermal analyser, and the synthetic resin PF/M were as new resin matrix to prepare semimetallic friction material, tribological performance test was carried on XD-MSM fixed speed type friction-wear testing machine in accordance with the GB_5763-2008. The results show that the heat resistance of composite PF/M and tribological performance of friction material are best when nanoMMT is 3% in the resin, the Carbon residue rate of PF/M is an increase of 37% compared with PF without nanoparticles at 600°C, thermal recession temperature of sample by the preparation of PF/M increases above 100°C, and it has stable friction coefficient, overall wear rate decreases 26%, especially in high temperature stage at 350°C, the wear rate decreases significantly, its wear rate decreases 30%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.