Abstract
The paper shows a comparative study of the influence of whitening additives (kaolin, TiO2 and СаСО3) on the production of decorative alkali-activated slag cement and mortars with a degree of whiteness of at least 70%; as well as their influence on the structure formation and evolution of physico-mechanical properties. According to results obtained, kaolin provides chemical bonding of Na+ into insoluble zeolite-like compounds; and CaCO3 densifies the structure and reduces shrinkage deformations. At the early stages of hardening (up to 7 days), the additions of kaolin and calcite, due to their significant amount (15 and 24%), reduces the compressive strength of the cement paste; nevertheless, at later ages (until 90 days) the difference in strength almost disappears. The high colourfastness and weather resistance of pigmented cements under the influence of ultraviolet radiation and freeze/thaw cycles has been established. A comparative assessment of the economic efficiency has shown that СаСО3 is the best cost-effective additive.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.