Abstract
Differences in the microstructure and magnetic properties of highly magnetostrictive cobalt ferrite resulting from the effects of different vacuum sintering temperatures and times have been investigated. A vacuum environment was chosen to allow direct comparison of results with air-sintered samples which are more often reported in the literature. It was found that vacuum sintering resulted in the development of a solid solution second phase with composition Co 1− x Fe x O 4 ( x∼0.33). There was a decrease in magnetostriction as a result of the formation of the second phase. Furthermore, differences in sintering temperatures were found to have a greater effect on the magnetostriction than differences in sintering times. It was found that the first order cubic anisotropy coefficient initially increased with both sintering temperature and time, before peaking and decreasing to its lowest measured value. The lowest anisotropy was therefore achieved with samples sintered at higher temperatures and longer times.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.