Influence of thermo-mechanical aging on fracture resistance and wear of digitally standardized chairside computer-aided-designed/computer-assisted-manufactured restorations

Abstract

ObjectivesTo investigate the influence of thermal cycling and mechanical loading (TCML) aging on fracture resistance and wear behavior of various chairside computer-aided-designed/computer-assisted-manufactured (CAD/CAM) premolar crowns cemented on standardized tooth abutments. MethodsEighty chairside CAD/CAM crowns were prepared using lithium disilicate (IPS e.max CAD; EM), zirconia-infiltrated lithium silicate (Celtra Duo; CD), polymer-infiltrated ceramic network (Vita Enamic; VE), and resin nanoceramics (Cerasmart; CS) (n = 20). The specimens were divided into two groups (n = 10). In one group, they were subjected to TCML: thermocycling (6000 cycles in distilled water at 5–55 °C) and mechanical loading (50 N for 1.2 × 106 cycles), while in control group they were stored in distilled water (37 °C for 24 h). The fracture load, height loss, and volume wear of the crowns were measured after TCML. Fractography was performed on fractured specimens. Data were analyzed using analysis of variance and multiple comparison tests (α=0.05). ResultsThe mean fracture loads of EM and CD were significantly higher than those of EC and CS (p<0.05). There was no significant change in the fracture load of any CAD/CAM crowns after TCML (p>0.05). CS exhibited a significantly higher volume wear than the other materials investigated. The wear tracts of all TCML crowns acted as failure origins during the fracture test. ConclusionsThe fracture resistance of glass-ceramic CAD/CAM crowns was significantly higher than that of resin composite crowns. A 5-year TCML aging did not affect the fracture resistance of CAD/CAM crowns investigated. However, TCML treatment produces a larger wear track in CS than in other materials. Clinical SignificanceAppropriate chairside CAD/CAM restorative material should be selected for successful clinical practice after considering the fracture and wear resistance of the crowns.