Polycrystalline cubic boron nitride (PcBN) composites were fabricated by spark plasma sintering (SPS). The SiC, Si3N4 and Si/B were used as binder. The effects of SPS sintering process parameters, such as the sintering temperature, holding time, heating rate and binder composition, on the properties of PcBN samples were investigated. PcBN composite with a hardness of 23.12GPa was fabricated efficiently by SPS. The hardness of PcBN sample increased first and then decreased with the increase of sintering temperature. As the holding time was 20 min, the hardness of PcBN sample was the highest. The PcBN performance at the heating rate of 50 °C/min was significantly better than that of 100°C /min. When the binder component of SiC, Si3N4, and Si was 63%:27%:10%, the hardness of PcBN was the highest. With an addition of Si, the PcBN samples had higher hardness than that of B.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.