Abstract
The subject of the work was to study the effect of Si alloying addition to the aluminum on the bond strength properties, wettability, and structure of interface in the AlSi11/Al2O3 joints. Taking advantage of the sessile drop method, the wetting of alumina substrates by liquid AlSi11 alloy or Al was studied. The sessile drop tests were carried out in the temperature range between 1023 and 1223 K, under a vacuum of 0.2 mPa for 30 or 120 minutes of contact. The shear strength results demonstrated significant improvement of shear strength of AlSi11/Al2O3 joints due to the application of silicon as an alloying addition to aluminum. Microstructural investigations of interface indicated that the silicon crystals were formed at the AlSi11/Al2O3 interface, which influenced the strengthening of these joints. A conclusion could be drawn, that the interface structure influenced the increase of the shear strength of AlSi11/Al2O3 joints.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.