Abstract
A study has been carried out into the influence of the proportion of SiCp and the matrix composition of four aluminium metal matrix composites (A360/SiC/10p, A360/SiC/20p, A380/SiC/10p and A380/SiC/20p) on their salt fog corrosion behaviour. The matrix of the A360/SiC/xxp composites is virtually free of Ni and Cu while the A380/SiC/xxp matrix contains 1.39 - 1.44 wt-%Ni and 3.13 - 3.45 wt-%Cu. The kinetics of the corrosion process were studied using gravimetric tests. The nature of corrosion products was analysed by SEM and low angle XRD before and after accelerated testing to determine the influence of microstructural changes on corrosion behaviour during exposure to the corrosive environment. The extent of the corrosion damage to the Al/SiC composites depended on the concentration of nucleation sites and the matrix composition. One of these nucleation sites is in the interface region between the matrix and the particles. The corrosion process was influenced more by the concentration of alloy elements in the matrix than by the proportion of SiCp reinforcement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.