Abstract
Alumina ceramics with optimized microstructures and mechanical properties were obtained by the attractive digital lighting processing (DLP) additive manufacturing methodology in the present study. A acrylate-based resin system was designed for the alumina powders with a mean particle size of 0.5 μm. The influence of oligomer on the viscosity and polymerization kinetics of the ceramic suspensions has been elaborately discussed by rheology, curing depth and photo-DSC characterizations. The results indicated that the introduction of oligomer has improved the cross-linking density of resins and decreased the critical dose of energy for resin polymerization, which contributed to a tougher ceramic-resin slice with higher dimensional accuracy. Densifying processes including debinding and high temperature sintering of the ceramic parts were conducted according to the TG-DTA characterizations, alumina ceramics with uniform microstructures and eliminated delamination or intralaminar cracks were finally obtained. The flexural strength was 471 MPa for the ceramics obtained from the resin composition containing 20 wt% oligomer, Weibull modulus for the ceramics were determined to be 17.31 by evaluating thirty all sides polished ceramics, indicating the highly uniform property of the ceramics fabricated by DLP additive manufacturing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.