Abstract
Ceramic cores are essential intermediate mediums in casting superalloy hollow turbine blades. The developing of additive manufacturing (AM) technology provides a new approach for the preparation of ceramic cores with complex structure. In this study, alumina oxide (Al2O3) ceramic cores with fine complex geometric shapes were fabricated by digital light processing (DLP) in high resolution. The maximum solid content of 70 vol% of ceramic slurry was adopted in the printing process, which is important for the regulation of deformations and mechanical properties. The effects of the printing parameters, including exposure intensity, printing layer thickness and sintering temperature on the microstructures and mechanical properties of printed samples were investigated. The decrease of residual stress and similar shrinkage in X, Y, and Z directions could be obtained by adjusting the printing parameters, which are crucial to prepare complex ceramic cores with high quality. Besides, the flexure strength and open porosity of ceramic cores reached 34.84 MPa and 26.94%, respectively, which were supposed to meet the requirement of ceramic cores for the fabrication of superalloy blades.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.