Abstract
This paper presents the effects of using the refill friction stir spot welding (RFSSW) technique on the mechanical properties and microstructure of aluminum AA5052 and AA6061-T3. Specimens were first prepared from AA5052 sheet of thickness 2 mm and AA6061-T3 of 1.6 mm, for chemical analysis and mechanical tests. Workpieces were then stir spot welded by RFSSW at four rotational speeds (2000, 2500, 3000 and 4000 rpm) using two tool pin diameters (5 and 7 mm) to carry out the tensile shear tests. Microhardness testing was conducted at the best conditions along the cross-section of the welded specimens, as well as microstructure examination. The results of the tensile shear tests manifested that, for AA5052 and AA6061-T3 at the tool rotational speeds 2000 rpm and 3000 rpm, respectively, using a tool pin of 7 mm the ultimate tensile shear force was slightly higher than at other speeds in both diameters of tool pin (5 and 7 mm). However, the microhardness results displayed a W-shape at the best conditions. Finally, the microstructure inspection revealed the morphology of the major zones of the weld joint.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.