Abstract
The nano-crystalline rare earth (Sm3+, Dy3+) substituted MgFe2O4 with composition Mg[(Sm)0.6(Dy)0.4]xFe2-xO4 [x varies from 0.0 to 0.3 in steps of 0.05] have been prepared by chemical combustion route. X-ray diffraction analysis confirmed the formation of the spinel cubic phase as a major phase along with the perovskite ortho-ferrite phase as a minor phase in all the samples except MgFe2O4. The room temperature magnetic properties of these samples have been investigated. It has been observed that with an increase in substitution of rare-earth ions (Sm3+, Dy3+), for iron in MgFe2O4, initial permeability increases, attain peak value for the composition with x = 0.15, and decreases for higher substitution concentrations. The microwave absorption performance of the Mg[(Sm)0.6(Dy)0.4]xFe2-xO4 systems have been investigated. The reflection coefficients are found to be higher as compared to MgFe2O4 whereas Voltage Standing Wave Ratio (VSWR) found to be lower. Overall investigations indicate Mg[(Sm)0.6(Dy)0.4]0.15Fe1.85O4 is a promising candidate for microwave device fabrication.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.