Abstract
Pulsed Nd:YAG laser beam welding was performed at five different power levels (360 W, 380 W, 400 W, 420 W and 440 W), and the relationship between microstructure and nano creep behaviour was investigated for Ti5Al2.5Sn alloy. Microstructural analysis indicated a reduction in grain size in fusion zone, with an increase in the average laser power. In the fusion zone (FZ) of all the beads, acicular α and ά martensite were observed and confirmed by SEM analysis. Due to the formation of the α and ά phases during welding, the microhardness and nanohardness in the FZ increased by ∼71% and ∼58%, respectively, above that of the base alloy. Nano creep analysis suggested diffusional creep as the deformation mechanism in all the beads, except the one performed at an average power of 440 W since its stress exponent was less than 2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.