Abstract
Continuous carbon-fibre (CCF) additive manufacturing of composites has significant potential for production of optimised structures. However, stiffness and strength in parts are often significantly lower than manufacturer material data. For thermoset-impregnated CCF, post-consolidation of specimens has greatly increased strength. In this contribution, the effect of post-consolidation for thermoplastic CCF material is presented. Specimens were manufactured on a commercial AM CCF printer and post-consolidation was performed by rapid compression moulding. Porosity was evaluated by X-ray Computed Tomography (CT) and a significant reduction from 5.3vol.% to 1.1vol.% was yielded.Experimental testing is performed in four-point bending with as-printed and post-consolidated samples. Bending stiffness and strength data was obtained. The results show that the bending strength was below expectations in as-printed specimens. Finite Element Analysis indicates that snap-buckling of a small number of outer layers can lead to such a reduced apparent bending strength, and CT scans of fracture surfaces of as-printed specimens reveal the presence of interlaminar debonding. It is shown that post-consolidation highly improves the interlaminar bond, yielding experimentally obtained strength values close to nominal material strength, and the expected kink-band compressive failure is achieved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.