Abstract

Grain boundary diffusion coefficients of {sup 57}Co and {sup 59}Co in polycrys. NiO, NiO bicrystal, and polycrys. Fe{sub 3}O{sub 4} were determined at various oxygen pressures at 750 C. For NiO, the low oxygen pressure region ( 10{sup {minus}15} MPa, the diffusion increased with pressure, owing to vacancy type diffusion. D{sub gb} of Co ions in Fe{sub 3}O{sub 4} is proportional to pO{sub 2}{sup {minus}2/3} in the low pressure region and to pO{sub 2}{sup 2/3} in the high pressure region, indicating similar mechanisms in the grain boundary diffusion and volume diffusion. Ratio of D{sub gb}/D was about 10{sup 3}.