Abstract
PLZT thin films were prepared by a dip coating process using Pechini's method, also known as polymeric precursor method. The PLZT solution was obtained from a mixture of the individual cation solutions and the process to prepare each solution is based on metallic citrate polymerization. The viscosity of the PLZT solution was adjusted at 40 cP while the ionic concentration was adjusted at 0.1 M. PLZT solutions were deposited on silicon (100) and platinum coated silicon (100) substrates with withdrawal speed at 5 mm/min. The coated substrates were thermally treated with a heating rate of 1 °C/min up to 300 °C and 5 °C/min up to 650 °C in order to obtain homogeneous and cracks free films. The influence of oxygen flow on crystallization and morphology of PLZT (9/65/35) thin film is discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.