Abstract
AA2024 T3 alloy specimens have been anodised in tartaric acid/sulphuric media and tartaric acid/sulphuric media containing sodium molybdate; molybdate species were added to the anodising bath to enhance further the protection provided by the porous anodic film developed over the macroscopic alloy surface. Morphological characterisation of the anodic films formed in both electrolytes was undertaken using scanning electron and transmission electron microscopies; the chemical compositions of the films were determined by Rutherford backscattering spectroscopy that was complemented by elemental depth profiling using rf-glow discharge optical emission spectrometry. The electrochemical behaviour was evaluated using potentiodynamic polarisations and electrochemical impedance spectroscopy; the corrosion performance was examined after salt spray testing. The porous anodic film morphology was little influenced by the addition of molybdate salt, although thinner films were generated in its presence. Chemical composition of the anodic film was roughly similar; however, addition of sodium molybdate in the anodizing bath resulted in residues of molybdate species in the porous skeleton and improved corrosion resistance measured by electrochemical techniques that was confirmed by salt spray testing.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.